Nguyen , T. M., Le , H., Le , H. T., Tran , T. H., Nguyen , D. H., Pham , T. L. H., Tran , T. T., Tran , T. T., Nguyen , T. H. P., & Le , X. C. (2014). Preparation of silver nanoparticles by gamma Irradiation method using chitosan as stabilizer. Nuclear Science and Technology, 4(3), 43-46. https://doi.org/10.53747/jnst.v4i3.235

Preparation of silver nanoparticles by gamma Irradiation method using chitosan as stabilizer

Nguyen Tan Man1, Le Hai1, Le Huu Tu1, Tran Thu Hong1, Nguyen Duy Hang1, Pham Thi Le Ha1, Tran Thi Thuy1, Tran Thi Tam1, Nguyen Trong Hoanh Phong1, Le Xuan Cuong1
1 Nuclear Research Institute, Nguyen Tu Luc Street, Dalat, Vietnam

Main Article Content

Abstract

Silver nanoparticles were prepared from (Ag+) aqueous solution by the method of γ-ray irradiation using chitosan as stabilizer. The saturated conversion dose (Ag+ à Ago) determined by UV-Vis spectroscopy was found to be about 16 kGy. The UV-Vis spectrum showed that an absorption peak at λmax = 400 nm due to surface plasma resonance. The image of transmission electron microscopy (TEM) showed that the silver nanoparticles were mostly spherical in shape and the average diameter was of about ~ 12 nm. The prepared colloidal silver nanoparticles solution was in good stability during storage time.

Article Details

Keywords

γ-ray irradiation, silver nanoparticles, chitosan

References

[1] D. Mei, “Radiation effects on nanoparticles, Emerging applications of radiation in nanotechnology”, IAEA-TECHDOC-1438, Vienna, Austria, pp. 125-135, (2005).
[2] T. Li, H. G. Park, S.H. Choi, “γ-Irradiation-induced preparation of Ag and Au nanoparticles and their characterizations”, Materials Chemistry and Physics, 105, pp. 325-330, (2007).
[3] D. Long, G. Wu, S. Chen, “Preparation of oligochitosan stabilized silver nanoparticles by gamma irradiation”, Radiation Physics and Chemistry, 76, pp. 1126-1131, (2007).
[4] B. D. Du, et al., “Preparation of colloidal silver nanoparticles in poly (N-vinyl pyrrolidone) by γ-irradiation”, Journal of Experimental Nanoscience, 3, pp. 207-213, (2008).
[5] P. Chen, L. Song, Y. Liu and Y. Feng, “Synthesis of silver nanoparticles by γ-ray irradiation in acetic acid solution containing chitosan”, Radiation Physics and Chemistry, 76, pp. 1165-1168, (2007).
[6] H. J. Prat et al., “A new composition of nanosized sillica-silver for control various plant diseases”, The Plant Pathology Journal, 22, pp. 295-302, (2006).
[7] A. Sileikaite et al., “Analysis of silver nanoparticles produced by chemical reduction of silver salt solution”, Material Sciences, 12, pp. 287-291, (2006).
[8] D. V. Phu et al., “Synthesis and antimicrobial effects of colloidal silver nanoparticles in chitosan by γ-irradiation”, Journal of Experimental Nanoscience, 5, pp. 169-179, (2010).
[9] R. Yoksan, S. Chirachanchai, “Silver nanoparticles dispersing in chitosan solution: Preparation by γ-ray irradiation and their antimicrobical activities”, Materials Chemistry and Physics, 115, pp. 296-302, (2009).
[10] N.M. Huang et al., “γ-ray assisted synthesis of silver nanoparticles in chitosan solution and the antibacterial properties”, Chemical Engineer Journal, 155, pp. 499-507, (2009).